TECHNICAL DATA

Appearance: Powder
Packaging: 25 kg Paper Bag
Color: White, Gray
Consumption: 2.5-5kg / m2
Warehouse: Store in a dry place on wooden palette
Self storage: 12 months from date of production
Volume weight: 1.8 gr / cm3
Floody: Unflammable
Water: 6-7 liters of water per 25 kg
pH of mix: 12
Application temperature: + 5 ° C to + 35 ° C
Correction time: 35-40 min
Wall joints: After 8 to 12 hours
Flow filling: After 24 hours
Definition : Non-deformable
Breakable: After 24 hours
Pressure resistance:> 12 N / mm2
Concrete adhesives:> 1 N / mm²
Conductive adhesion after 28 days (normal conditions): ≥ 1 N / mm²
Conductive adhesion after immersion: ≥ 1 N / mm²
Adhesives after heat reaction: ≥ 1.5 N / mm²
Adhesives after freeze-thaw cycles: ≥ 1 N / mm²

Tile adhesive, cement based product (C), with very high flexibility (S1), improved adhesive strength (2), resistant to slipping (T) and long workability time (E). It is applied to layers with a thickness up to 15 mm. Classified as C2TES1 adhesive according to EN 12004. Specifications: Cement based adhesive, consisting of high quality carbonate and marble sands with selected granulometry, synthetic resins and specific additives. Thishigh technology in granulometric distribution and its special components, give this product excellent features in flexibility and workability, which makes this adhesive ideal for adhesion of marble tiles, natural stone, granite, mosaic etc.Specifications: Cement based adhesive, i consisting of high quality marble sand with selected granulometry, synthetic resins and special modified additives. Advanced technology in granulometric dispersion and special ingredients give the product excellent quality in flexibility and workability, making this adhesive ideal for adhesion of marble, natural stone, granite, mosaics. APPLICATION FIELD marble, stone slabs, mosaics, high spice slabs on cement-based supports, for floors and walls, indoors and outdoors where there is a high moisture content. Recommended for facades, terraces, central heating environments, environments that are part of vibrations, continuous printing, also for tile adhesion (in this case the tiles must be durable and non-slip), for environments industrial, for corrugated and unstable supports (due to its high elasticity and deformability).

MIXED PREPARATION METHOD

Mix 6-7 liters of pure water with 25 kg ADESIFLEX, mix the mass created with an electric mixer until formed. a homogeneous, grain-free mass. Leave to rest for 10 minutes and then mix again before use. The shelf life of the mix is ​​2-3 hours under normal temperature conditions (20 ° C). have reached maturity in advance. Approximately traditional cement-based floors with normal hardening time should have a shelf life of at least 28 days, and traditional plaster plates should dry for at least 14 days. Large bumps or cracks should be adjusted in advance. All types of supports should be mechanically cleaned before applying the product. Before applying the product, the surface of the support should be moistened in order for the product to adhere better to it.

Initially the product is recommended to be coated with the right part of the product to have a uniform distribution and then with the toothed part. The application is made with a suitable screed depending on the type of tile being laid. Tile laying is done by exerting a slight pressure on the tile making sure the tile is covered throughout the cough surface. The opening time of the product under normal atmospheric conditions is 35 minutes for temperatures of 23 ° C. Atmospheric conditions can affect the drying time of the product. Care should be taken that the glue does not form a film surface. Otherwise it is necessary to pass the cough goods once again. It is not advisable to place the tiles with kissing joints. The tiles are placed in such a way that they are appropriate to their dimensions. At the joint surfaces with vertical walls a distance of 5 mm should be left.