Form: Powder
Packaging: In sacks of 25 kg on pallets of 1350 kg
Color: Grey, White
Consumption for small formats: 2-3 kg / m2
Consumption for large formats::4-5kg / m2
Storage: Store in a dry place on wooden pallets.
Storage time: 12 months from the manufacture date
Density: : 1.8 gr/cm3
Reaction to fire: Class A1
Water demand: 7-8 liters of water per 25 kg
pH of the mixture: 13
Application temperature: +5°C to +35°C
Adjustability time: 35-40 min
Grouting on the walls: After 8 to 12 hours
Grouting on the floor: After 24 hours
Set to light foot traffic: After 24 hours
Adhesive strength after 28 days: ≥ 1 N/mm²
Adhesive strength after water immersion: :≥ 1 N/mm²
Adhesive strength after heating reaction: ≥ 1 N/mm²
Adhesive strength after thaw-freeze cycles: ≥ 1 N/mm²
Adhesive strength after 30 min: ≥ 0.5 N/mm²
Slippery: ≤ 0.5 mm

Tile adhesive, cement based product (C), with very high flexibility (S1), improved adhesive strength (2),
resistant to slipping (T) and long workability time (E). It is applied for layers with a thickness up to 15 mm. Classified as C2TES1 adhesive according to standard EN 12004. Specifications: Cement based adhesive, composed of high quality carbonate and marble sands with a selected granulometry, synthetic resins and specific additives. This
high technology in the granulometric distribution and its special components, give to this product excellent features in flexibility and workability, which makes this adhesive ideal for adhesion of the marble tiles, natural stone, granite, mosaic etc


Suitable for the adhesion of marble tiles, stone tiles, mosaics, glass bricks, tiles with low absorption and
high shim, for external and internal floors and walls in humidity presence. Recommended for high facades, terraces, for central heating facilities, for facilities that are part of the ongoing vibrations pressures, also
suitable for adhesion of tile on tile (in this case tiles should be fixed and stable), for industrial environments,
for unstable and undulations supports (as a result of high elasticity and high rate of deformation).


Mix 25 kg ADESIFLEX with7-7,5 liters of clean water through an electric mixer, until is achieved a homogenous mass and without grains. Leave the mass at rest for 10 minutes and mix it again before usage. Workability time, in normal temperature conditions (23°C) is 2-3 hours.


Cement based supports should be regular, resistant and stable, cleaned, without oils, and without paint residues, and must have reached the time of maturity. Approximately, the traditional cement-based floors with normal induration time should have maturation time at least 28 days; supports with traditional plaster should
dry for at least 14 days. Disparities or cracks should be adjusted in advance. All types of the supports must be
cleaned before the application of the product, mechanically. Before applying the product, the surface of the substrate must be wet in order to create a better adhesion with it.

Initially, it is recommended to apply the product with the smooth part of the screed to have a more uniform
distribution and then with the serrated part. For the application it is used a suitable screed depending on the type of the tile that the product is applied. Tiles are placed by using a slight pressure on tile in order to
make sure that the surface of the tile is covered with adhesive. Opening time of the product under normal
temperatures is 35 minutes for 23°C. Weather conditions may affect the drying time of the product. Take care
because the adhesive should not create a surface of film. Otherwise it is necessary to pass once again the
screed into the adhesive. It is not advisable to lay the tiles with the joint
grouts. Tiles are placed in such a way as to be suited to their dimensions